Solid Wire for Submerged Arc Welding 埋弧焊实芯焊丝 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Item Code |
Equivalent Norm |
Chemical Composition of Wire (%) |
Mechanical Properties of Deposited Metal (Typical) |
Application |
Remark |
|
C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
Cu |
Combined Flux |
Welding Posititon |
Current |
Equivalent Norm |
Yield Point ReL (MPa) |
Tensile Strength Rm (MPa) |
Elongation A (%) |
Akv value (J) |
Temp. (℃) |
Joule |
CHW-S1 |
AWS A5.17 EL12 GB H08A EN 756 S1 |
Standard Typical |
0.04-0.14 0.07 |
0.25-0.60 0.40 |
≤0.10 0.018 |
≤0.030 0.011 |
≤0.030 0.014 |
— |
— |
— |
≤0.35 0.10 |
CHF43 |
F |
DC+ or AC |
AWS A5.17 F6A0/EL12 |
360 |
450 |
29 |
-20 |
80 |
Suitable forwelding structures fabricated by 450MPa grade steel, e.g. LPG cylinder or ship structures as same strength |
CHF43/CHW-S1 approved by CCS, LR, ABS, GL, BV & DNV |
CHF501 |
F |
DC+ or AC |
AWS A5.17 F7AZ/EL12 |
425 |
530 |
29 |
0 |
70 |
CHW-S2 |
AWS A5.17 EM12 EN 756 S2 |
Standard Typical |
0.06-0.15 0.066 |
0.80-1.25 0.88 |
≤0.10 0.022 |
≤0.030 0.013 |
≤0.030 0.010 |
__ 0.02 |
__ 0.021 |
— |
≤0.35 0.025 |
CHF301 |
F |
DC+ or AC |
AWS A5.17 F7A0/EM12 |
415 |
510 |
25 |
-20 |
70 |
For welding 450MPa-500MPa grade structures, such as boiler, bridges, pressure vessels as well as LPG cylinders. |
CHF101/CHW-S2 approved by CCS & NK |
CHF101 |
F |
DC+ or AC |
AWS A5.17 F6A4/EM12 |
360 |
480 |
31 |
-40 |
115 |
CHW-S3 |
AWS A5.17 EH14 GB H10Mn2 |
Standard Typical |
0.10-0.20 0.13 |
1.70-2.20 1.87 |
≤0.10 0.05 |
≤0.030 0.011 |
≤0.030 0.013 |
__ 0.018 |
__ 0.005 |
— |
≤0.35 0.020 |
CHF101 |
F |
DC+ or AC |
AWS A5.17 F7A2/EH14 |
440 |
530 |
30 |
-30 |
150 |
Suitable for fabricating 500MPa-550MPa grade strength structures, such as ship hulls, bridges, pressure vessels and H-beam structures. |
CHF101/CHW-S3 approved by CCS, LR, ABS,GL,BV,DNV,NK & CWB |
CHF105 |
F |
DC+ |
AWS A5.17 F7A4/EH14 |
430 |
510 |
28 |
-40 |
120 |
CHW-S4 |
AWS A5.17 EM13K |
Standard Typical |
0.06-0.16 0.089 |
0.90-1.40 1.84 |
0.35-0.75 0.57 |
≤0.030 0.016 |
≤0.030 0.016 |
— |
— |
— |
≤0.35 0.052 |
CHF101 |
F |
DC+ or AC |
AWS A5.17 F7A2/EM13K |
500 |
585 |
30 |
-30 |
95 |
For welding structures made by 500MPa grade carbon steel or low alloy steels , such as boiler, bridges, pressure vessels etc. |
|
CHW-S5 |
AWS A5.17 EH12K DIN SG3 |
Standard Typical |
0.06-0.15 0.084 |
1.50-2.00 1.84 |
0.25-0.65 0.65 |
≤0.025 0.009 |
≤0.025 0.020 |
— |
— |
— |
≤0.35 0.046 |
CHF101 |
F |
DC+ or AC |
AWS A5.17 F7A0/EM11K |
520 |
665 |
23 |
-20 |
55 |
For welding structures made by 450MPa-500MPa grade carbon steel or low alloy steels , such as boiler, bridges, pressure vessels etc. |
|
CHW-S6 |
AWS A5.17 EH11K DIN SG2 |
Standard Typical |
0.07-0.15 0.08 |
1.40-1.85 1.49 |
0.80-1.15 0.84 |
≤0.030 0.009 |
≤0.030 0.014 |
— |
— |
— |
≤0.35 0.28 |
— |
F |
DC+ |
— |
— |
— |
— |
— |
— |
For welding structures made by 450MPa-500MPa grade carbon steel or low alloy steels , such as boiler, bridges, pressure vessels etc. |
|
CHW-S7 |
AWS A5.23 EA3 EN 756 S4Mo |
Standard Typical |
0.05-0.17 0.064 |
1.65-2.20 1.70 |
≤0.20 0.13 |
≤0.025 0.007 |
≤0.025 0.008 |
— |
— |
0.45-0.65 0.50 |
≤0.35 0.13 |
CHF115 |
F |
DC+ |
AWS A5.23 F10P0-EA3-A3 |
630 |
735 |
23 |
-20 |
100 |
Suitable for fabricating important structures made by 690MPa grade low alloy steels, e.g. BHW35, WEL-TEN70, HW56, SM570, etc. which need high toughness. |
|
CHF113 |
F |
DC+ |
AWS A5.23 F9P4-EA3-A3 |
600 |
690 |
24 |
-40 |
60 |
CHW-S8 |
AWS A5.23 EB3 EN 12070 S CrMo2 |
Standard Typical |
0.05-0.15 0.09 |
0.40-0.80 0.80 |
0.05-0.30 0.15 |
≤0.025 0.010 |
≤0.025 0.011 |
2.25-3.00 2.61 |
— |
0.90-1.10 1.01 |
≤0.35 0.10 |
CHF603 |
F |
DC+ |
AWS A5.23 F8PZ-EB3-B3 |
475 |
570 |
22 |
20 |
85 |
Widely be used in welding important thick hull pressure vessels of nuclear reactors as well as important steam pipes of thermal power station. |
|
CHW-S9 |
AWS A5.23 EA4 EN 756 S2Mo |
Standard Typical |
0.05-0.17 0.08 |
1.20-1.70 1.24 |
≤0.20 0.21 |
≤0.025 0.008 |
≤0.025 0.011 |
__ 0.023 |
__ 0.020 |
0.45-0.65 0.47 |
≤0.35 0.20 |
CHF105 |
F |
DC+ or AC |
AWS A5.23 F8A2-EA4-A2 |
530 |
623 |
23 |
-30 |
70 |
Suitable for important structures fabricated by 600MPa grade low alloy steels such as cranes, heavy trucks & engineering machinery,bridges and high pressue vessels, etc. |
|
CHW-S9CG |
AWS A5.23 EA4 EN 756 S2Mo |
Standard Typical |
0.05-0.17 0.060 |
1.20-1.70 1.30 |
≤0.20 0.20 |
≤0.025 0.010 |
≤0.025 0.012 |
Cr 0.25 Ti 0.08 |
__ 0.020 |
0.45-0.65 0.47 |
≤0.35 0.20 |
CHF101 |
F |
DC+ |
AWS A5.23 F8P2-EA4-A4 |
545 |
635 |
26 |
-30 |
85 |
It is suitable for welding 550MPa-600MPa grade flawless steels especially widely be used on the huge petroleum storage tanks. |
|
CHW-S10 |
AWS A5.23 EF3 GB H10Mn2NiMoA |
Standard Typical |
0.10-0.18 0.10 |
1.70-2.40 1.81 |
≤0.30 0.20 |
≤0.025 0.009 |
≤0.025 0.010 |
__ 0.20 |
0.70-1.10 0.94 |
0.40-0.65 0.65 |
≤0.35 0.15 |
CHF105 |
F |
DC+ |
AWS A5.23 F10P2-EF3-F3 |
670 |
760 |
20 |
-30 |
70 |
Suitable for fabricating important structures made by 690MPa-720MPa grade high strength low alloy steels. |
|
CHW-S11 |
AWS A5.23 EB2 EN 12070 S CrMo1 |
Standard Typical |
0.07-0.15 0.95 |
0.45-1.00 0.75 |
0.05-0.30 0.15 |
≤0.025 0.007 |
≤0.025 0.013 |
1.00-1.75 1.36 |
— |
0.40-0.65 0.48 |
≤0.35 0.22 |
CHF105 |
F |
DC+ |
AWS A5.23 F8P2-EB2-B2 |
550 |
640 |
25 |
-30 |
140 |
For welding structures fabricated by 1.2Cr-0.5Mo pearlitic heat resistant steels and equipments of petroleum chemical industry made by 13CrMoA, 15CrMo, 12CrMo. |
|
CHW-S12 |
AWS A5.17 EM12K EN 756 S2Si |
Standard Typical |
0.05-0.15 0.08 |
0.80-1.25 1.06 |
0.10-0.35 0.22 |
≤0.030 0.014 |
≤0.030 0.016 |
___ 0.025 |
__ 0.026 |
— |
≤0.35 0.10 |
CHF101 |
F |
DC+ or AC |
AWS A5.17 F7A4/EM12K |
420 |
510 |
31 |
-40 |
110 |
Suitable for fabricating normal strength structures made by 450MPa-500MPa grade mild steels, e.g.LPG cylinder. |
|
CHF301 |
F |
DC+ or AC |
AWS A5.17 F7A0/EM12K |
430 |
540 |
28 |
-20 |
70 |
CHW-S13 |
AWS A5.23 ENi3 |
Standard Typical |
≤0.13 0.09 |
0.60-1.20 1.00 |
0.05-0.30 0.15 |
≤0.020 0.009 |
≤0.020 0.011 |
≤0.15 0.03 |
3.10-3.80 3.45 |
— |
≤0.35 0.20 |
CHF105DR |
F |
DC+ |
AWS A5.23 F7P10-ENi3-Ni3 |
440 |
560 |
28 |
-70 |
100 |
Suitable for welding structures made by low temperature service alloy steels, which contains 2.5Ni or 3.5Ni. |
|
CHW-S16 |
AWS A5.23 EA2 |
Standard Typical |
0.05-0.17 0.08 |
0.95-1.35 1.20 |
≤0.20 0.18 |
≤0.025 0.010 |
≤0.025 0.012 |
— |
— |
0.45-0.65 0.57 |
≤0.35 0.20 |
CHF101GX |
F |
DC+ |
AWS A5.23 F8A2-EA2-A2 |
530 |
625 |
23 |
-30 |
70 |
Suitable for welding 550MPa important high strength structures,especially for spiral or longitudinal welded huge diameter pipe made by X65, X70 steels.It could be four wire welding at same time and the welding speed is 1.70m-2.00m per minute. |
|
CHW-S18 |
AWS A5.17 EL8 |
Standard Typical |
≤0.10 0.07 |
0.25-0.60 0.44 |
≤0.07 0.018 |
≤0.030 0.011 |
≤0.030 0.014 |
— |
— |
— |
≤0.35 0.23 |
CHF501 |
F |
DC+ |
AWS A5.17 F7AZ-EL8 |
425 |
530 |
29 |
0 |
70 |
Suitable forwelding structures fabricated by 450MPa grade steel, e.g. LPG cylinder or ship structures as same strength. |
|
CHW-SG |
AWS A5.23 EG |
Standard Typical |
___ 0.025 |
___ 0.025 |
___ 0.025 |
___ 0.025 |
___ 0.025 |
— |
___ 0.025 |
— |
— |
CHF101GX |
F |
DC+ or AC |
Butt weld metal |
— |
650 |
— |
-20 |
180 |
Suitable for welding 550MPa important high strength tructures,which require extra lower S & P in weld metal, especially for spiral or longitudinal welded huge diameter pipe made by X65, X70 steels. |
|
Deposited metal |
450 |
540 |
29 |
-20 |
160 |
CHW-STH550Ⅲ |
AWS A5.23 EG |
Standard Typical |
__ 0.066 |
__ 1.35 |
__ 0.11 |
__ 0.009 |
__ 0.010 |
__ 0.42 |
__ 0.58 |
— |
__ 0.22 |
CHF101NQ |
F |
DC+ or AC |
TH550-NQ-Ⅲ |
540 |
630 |
26 |
-40 |
120 |
For welding marin or railway containers, railway wagons, tank cars as well as locomotives, which fabricated by atmospheric corrosion and infection resistance low alloy steels. |
|
CHW-308 |
AWS A5.9 ER308 |
Standard Typical |
≤0.08 0.05 |
1.00-2.50 1.79 |
0.30-0.65 0.33 |
≤0.030 0.010 |
≤0.030 0.012 |
19.50-22.00 19.72 |
9.00-11.00 10.14 |
≤0.75 0.10 |
≤0.75 0.11 |
CHF601 |
F |
DC+ |
— |
— |
540 |
40 |
— |
— |
For welding 18%Cr-8%Ni stainless steel. |
|
CHW-308L |
AWS A5.9 ER308L |
Standard Typical |
≤0.03 0.024 |
1.00-2.50 1.82 |
0.30-0.65 0.34 |
≤0.030 0.013 |
≤0.030 0.016 |
19.50-22.00 19.76 |
9.00-11.00 9.83 |
≤0.75 0.14 |
≤0.75 0.13 |
CHF601 |
F |
DC+ |
— |
— |
530 |
42 |
— |
— |
For welding extra low carbon 18%Cr-8%Ni stainless steel. |
|
CHW-309 |
AWS A5.9 ER309 |
Standard Typical |
≤0.12 0.06 |
1.00-2.50 2.05 |
0.30-0.65 0.34 |
≤0.030 0.010 |
≤0.030 0.018 |
23.00-25.00 23.83 |
12.00-14.00 13.26 |
— |
≤0.75 0.10 |
CHF601 |
F |
DC+ |
— |
— |
540 |
38 |
— |
— |
For welding 22%Cr-12%Ni stainless steel. The weld metal shows a good heat resistance & corrosion resistance feature. Also it could be used in dissimilar steels. |
|
CHW-309L |
AWS A5.9 ER309L |
Standard Typical |
≤0.03 0.026 |
1.00-2.50 2.11 |
0.30-0.65 0.38 |
≤0.030 0.016 |
≤0.030 0.014 |
23.00-25.00 23.56 |
12.00-14.00 12.31 |
— |
≤0.75 0.13 |
CHF601 |
F |
DC+ |
— |
— |
530 |
39 |
— |
— |
For welding extra low carbon 24%Cr-13%Ni stainless steel. It could be used for root welding also. |
|
CHW-310 |
AWS A5.9 ER310 |
Standard Typical |
0.08-0.15 0.09 |
1.00-2.50 1.90 |
0.30-0.65 0.35 |
≤0.030 0.015 |
≤0.030 0.014 |
25.00-28.00 26.80 |
20.00-22.50 21.40 |
— |
≤0.75 0.12 |
CHF601 |
F |
DC+ |
— |
— |
560 |
40 |
— |
— |
For welding 25%Cr-20%Ni stainless steel. The weld metal shows a good heat resistance & oxidation resistance feature. |
|
CHW-316 |
AWS A5.9 ER316 |
Standard Typical |
≤0.08 0.04 |
1.00-2.50 1.88 |
0.30-0.65 0.33 |
≤0.030 0.013 |
≤0.030 0.018 |
18.00-20.00 19.27 |
11.00-14.00 12.70 |
2.00-3.00 2.26 |
≤0.75 0.11 |
CHF601 |
F |
DC+ |
— |
— |
540 |
38 |
— |
— |
For welding 18%Cr-12%Ni-2%Mo stainless steel. The weld metal has very good heat crack resistance character. |
|
CHW-316L |
AWS A5.9 ER316L |
Standard Typical |
≤0.03 0.020 |
1.00-2.50 1.85 |
0.30-0.65 0.38 |
≤0.030 0.010 |
≤0.030 0.015 |
18.00-20.00 18.73 |
11.00-14.00 12.50 |
2.00-3.00 2.36 |
≤0.75 0.10 |
CHF601 |
F |
DC+ |
— |
— |
530 |
39 |
— |
— |
For welding extra low carbon 18%Cr-12%Ni-2%Mo stainless steel. The weld metal has excellet heat crack resistance & corrosion resistance character. |
|
CHW-317 |
AWS A5.9 ER317 |
Standard Typical |
≤0.08 0.04 |
1.00-2.50 1.86 |
0.30-0.65 0.46 |
≤0.030 0.012 |
≤0.030 0.017 |
18.50-20.50 19.30 |
13.00-15.00 14.20 |
3.00-4.00 3.50 |
≤0.75 0.11 |
CHF601 |
F |
DC+ |
— |
— |
550 |
38 |
— |
— |
Suitable for fabricating stainless steel containers that resisting corrosion of vitriol,ammonia, sulfurous acid or salt, etc. |
|
CHW-347 |
AWS A5.9 ER347 |
Standard Typical |
≤0.08 0.06 |
1.00-2.50 1.84 |
0.30-0.65 0.41 |
≤0.030 0.018 |
≤0.030 0.020 |
19.00-21.50 19.40 |
9.00-11.00 9.50 |
___ Nb 0.89 |
≤0.75 0.12 |
CHF601 |
F |
DC+ |
— |
— |
550 |
39 |
— |
— |
For welding important resisting corrosion structures made by 1Cr18Ni9Ti stainless steels. |
|
CHW-410 |
AWS A5.9 ER410 |
Standard Typical |
≤0.12 0.10 |
≤0.60 0.47 |
≤0.50 0.42 |
≤0.030 0.011 |
≤0.030 0.016 |
11.50-13.50 11.80 |
≤0.60 0.20 |
— |
≤0.75 0.14 |
CHF601 |
F |
DC+ |
— |
— |
510 |
26 |
— |
— |
Hard facing surface of structures made of 0Cr13 or 1Cr13 stainless steels. |